Poly(ester amide) filler blends for modulation of coating properties

ABSTRACT

Provided herein is a PEA polymer blend and coatings or implantable devices formed therefrom.

CROSS-REFERENCE TO RELATED APPLICATION

This is a divisional application of U.S. application No. 10/976,551, filed on Oct. 29, 2004, issued as U.S. Pat. No. 7,390,497, the teaching of which is incorporated herein by reference in its entirety.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention generally relates to poly(ester amide) (PEA) polymer blends having a PEA polymer and a material or polymer capable of hydrogen-bonding with the PEA polymer, which have a glass transition temperature (T_(g)) higher than the PEA polymer and are useful for coating an implantable device such as a drug-delivery stent.

2. Description of the Background

Poly(ester amide) polymers are known for their relatively low glass transition temperatures. For example, co-poly-{[N,N′-sebacoyl-bis-(L-leucine)-1,6-hexylene diester]-[N,N′-sebacoyl-L-lysine benzyl ester]} (PEA-Bz) and co-poly{[N,N′-sebacoyl-bis-(L-leucine)-1,6-hexylene diester]-[N,N′-sebacoyl-L-lysine 4-amino-TEMPO amide]} (PEA-TEMPO) have a T_(g) of approximately 23° C. and 33° C., respectively.

Complications related to low T_(g) manifest themselves as reduced release rate control, potential sticking and adhesion to the delivery balloon, and reduced shelf life stability. Low T_(g) materials have higher drug permeabilities, which necessitates the use of greater amounts of polymer to control release rate of the drug. Moreover, the low T_(g) can enable the drug to diffuse within the coating. In other words, the drug configuration within a given coating can change with time until an equilibrium state is reached, resulting in release rate shifts. Low T_(g) materials also tend to be softer, they can be more adhesive to balloons, and are more prone to failure during mechanical perturbations such as crimping and expansion.

The embodiments of the present invention provide for methods addressing these issues.

SUMMARY OF THE INVENTION

Provided herein are poly(ester amide) (PEA) compositions that include one or more PEA polymers and a material capable of hydrogen bonding with the PEA molecules. The PEA compositions provided herein can form coatings that have improved stability, drug release rate, and mechanical characteristics. The PEA compositions can also be used to form the implantable device itself, one example of which is a stent.

In some embodiments, the PEA polymer blends can be used optionally with a biobeneficial material and/or optionally a bioactive agent to coat an implantable device. In some other embodiments, the PEA polymer blends can be used with one or more biocompatible polymers, which can be biodegradable, bioabsorbable, non-degradable, or non-bioabsorbable polymer.

The implantable device can be a stent that can be a metallic, biodegradable or nondegradable stent. The stent can be intended for neurovasculature, carotid, coronary, pulmonary, aorta, renal, biliary, iliac, femoral, popliteal, or other peripheral vasculature. The stent can be used to treat or prevent a disorder such as atherosclerosis, thrombosis, restenosis, hemorrhage, vascular dissection or perforation, vascular aneurysm, vulnerable plaque, chronic total occlusion, claudication, anastomotic proliferation for vein and artificial grafts, bile duct obstruction, ureter obstruction, tumor obstruction, or combinations thereof.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1 a, 1 b and 1 c are SEM (scanning electron micrographs) of stents coated with poly(ester amide) and PolyActive™. FIG. 1 a shows the SEM of the stents with coatings of configuration 1; FIG. 1 b shows the SEM of the stents with coatings of configuration 2, and FIG. 1 c shows the SEM of the stents with coatings of configuration 3. Configurations 1-3 are described in Example 1.

FIG. 2 shows the drug-release data of the stents as described in Example 1 in PBS-Triton system.

DETAILED DESCRIPTION

Provided herein are poly(ester amide) (PEA) compositions that include one or more PEA polymers and a material capable of hydrogen bonding with the PEA molecules. The PEA compositions provided herein can form coatings that have improved stability, drug release rate, and mechanical characteristics. The PEA compositions can also be used to form the implantable device itself, one example of which is a stent.

In some embodiments, the PEA polymer blends can be used optionally with a biobeneficial material and/or optionally a bioactive agent to coat an implantable device. In some other embodiments, the PEA polymer blends can be used with one or more biocompatible polymers, which can be biodegradable, bioabsorbable, non-degradable, or non-bioabsorbable polymer.

The implantable device can be a stent that can be a metallic, biodegradable or nondegradable stent. The stent can be intended for neurovasculature, carotid, coronary, pulmonary, aorta, renal, biliary, iliac, femoral, popliteal, or other peripheral vasculature. The stent can be used to treat or prevent a disorder such as atherosclerosis, thrombosis, restenosis, hemorrhage, vascular dissection or perforation, vascular aneurysm, vulnerable plaque, chronic total occlusion, claudication, anastomotic proliferation for vein and artificial grafts, bile duct obstruction, ureter obstruction, tumor obstruction, or combinations thereof.

Polymers Capable of Forming Hydrogen Bonds with poly(ester amide)

Hydrogen bonding is an important form of molecule-molecule interactions that occur between hydrogen atoms bonded to an atom with high electronic negativity, typically fluorine, oxygen and nitrogen, and the unshared electron pairs located on other electronegative atoms. A hydrogen bond can be generally described as X₁—H—X₂, where X₂ can be an electronic donor or acceptor and X₁ and X₂ are independently fluorine, oxygen, or nitrogen atoms or groupings.

The amide groups in the PEA polymer backbone can participate in hydrogen bonding as both donors and acceptors. This behavior is well known in nylon polymers. However, the stereochemistry of the PEA chain is such that a close packed arrangement, which would allow for hydrogen bonding between the polymer chains, does not occur. In order to elicit an interaction between PEA chains, polymeric fillers can be added to PEA. These fillers can serve as a bridge between PEA chains if they are capable of hydrogen bonding. In this way, the amide groups in the PEA chain can hydrogen bond to the filler, which, in turn, can hydrogen bond to another PEA chain, thereby reducing the mobility of the PEA polymer chains and thus increasing the effective T_(g) of the material.

As used herein, poly(ester amide) encompasses a polymer having at least one ester grouping and at least one amide grouping in the backbone. One example is the PEA polymer made according to Scheme I. Other PEA polymers are described in U.S. Pat. No. 6,503,538 B1. An example of the PEA polymer includes diacid, diol, and amino acid subunits, the pendant groups of which may or may not include biobeneficial moieties.

PEA polymers can be made by condensation polymerization utilizing, among others, diacids, diols, diamines, and amino acids. Some exemplary methods of making PEA are described in U.S. Pat. No. 6,503,538 B1.

Many polymers are capable of forming hydrogen bonds with the PEA polymer chain. To select a proper polymer filler, two conditions must be given: (1) it must be acceptable for the polymeric filler to be released, and (2) some hydrogen bonding polymers are hydrophilic and a very hydrophilic polymer will increase water absorption of the material, which lowers the T_(g) of the material, increases drug diffusivity, and lowers the strength, negating the desired effect of increasing T_(g) of the PEA material. Therefore, a preferred polymer filler will be capable of forming hydrogen bonds with the PEA polymer chain but will not substantially increase water absorption of the material. For example, such a polymer filler will have a hydrophicility close to or below about the hydrophicility of poly(vinyl alcohol).

T_(g) as used herein generally refers to the temperature at which the amorphous domains of a polymer change from a brittle vitreous state to a plastic state at atmospheric pressure. In other words, T_(g) corresponds to the temperature where the onset of segmental motion in the chains of the polymer occurs, and it is discernible in a heat-capacity-versus-temperature graph for a polymer. When an amorphous or semicrystalline polymer is heated, its coefficient of expansion and heat capacity both increase as the temperature rises, indicating increased molecular motion. As the temperature rises, the sample's actual molecular volume remains constant. Therefore, a higher coefficient of expansion points to a free volume increase of the system and increased freedom of movement for the molecules. The increasing heat capacity corresponds to increasing heat dissipation through movement.

As used herein, the term “low T_(g)” refers to a T_(g) of below about the T_(g) of PEA-BZ (T_(g)=23° C.) or below about the T_(g) of PEA-TEMPO (T_(g)=33° C.).

Suitable hydrogen bonding polymers can be biodegradable or non-degradable or durable polymers, or combinations thereof. Non-degradable polymers that may be blended with a PEA polymer must have a number-average molecular weight or weight-average molecular weight below approximately 40,000 Daltons to allow them to be secreted by the kidneys. Biodegradable polymers that may be blended with a PEA polymer must be able to degrade into fragments having a number-average or weight-average molecular weight below about 40,000 Daltons to allow them to be secreted by the kidneys. Specific non-degradable polymer candidates include, but are not limited to, polymers or copolymers of monomers containing a hydroxyl group, a carboxyl group or an amino group, examples of which are poly(vinyl alcohol), poly(vinyl alcohol-co-vinyl acetate), polyacrylic acid, poly(ethylene-co-acrylic acid), polymethacrylic acid, poly(ethylene-co-vinyl alcohol), poly(acrylamide), poly(hydroxypropyl methacrylamide), poly(2-hydroxyethyl methacrylate), poly(2-methoxyethyl methacrylate), poly(2-ethoxyethyl methacrylate), poly(2-methoxyethyl acrylate), poly(vinyl pyrrolidone), poly(pyrrole), (non-water soluble cellulose acetate, non-water soluble hydroxyethyl cellulose, non-water soluble hydroxypropyl cellulose, cellulose ethers such as methyl cellulose and ethyl cellulose, , poly(urethanes), poly(urethane-ureas), poly(ureas), poly(tetramethylene glycol), poly(propylene glycol), poly(ethylene glycol), and combinations thereof.

In some embodiments, biodegradable polymers capable of hydrogen bonding with PEA polymers can be, for example, poly(imino carbonates), peptides, gelatin, collagen, non-water soluble chitosan, agarose, elastin, poly(alginic acid), alginate, dextrose, dextran, poly(glutamic acid), poly(lysine), copolymers containing poly(ethylene glycol) and polybutylene terephthalate segments (PEG/PBT) (PolyActive™), poly(aspartic acid), poly(leucine), poly(leucine-co-hydroxyethyl glutamine), poly(benzyl glutamate), poly(glutamic acid-co-ethyl glutamate), poly(amino acids), or a combination thereof. poly(ortho esters), poly(anhydrides), poly(D,L-lactic acid), poly (L-lactic acid), poly(glycolic acid), copolymers of poly(lactic) and glycolic acid, poly(phospho esters), poly(β-hydroxybutyrate), poly(caprolactone), poly(trimethylene carbonate), poly(oxaesters), poly(oxaamides), poly(ethylene carbonate), poly(propylene carbonate), poly(phosphoesters), poly(phosphazenes), copolymers thereof with PEG, or combinations thereof.

In some embodiments, the hydrogen-bonding filler can be a block copolymer having flexible poly(ethylene glycol) and poly(butylene terephthalate) blocks (PEGT/PBT) (e.g., PolyActive™). PolyActive™ is intended to include AB, ABA, BAB copolymers having such segments of PEG and PBT (e.g., poly(ethylene glycol)-block-poly(butyleneterephthalate)-block poly(ethylene glycol)(PEG-PBT-PEG). PolyActive™ (commonly expressed in the formula XPEGTMPBTN where X is the molecular weight of the PEG segment, M is weight percentage of PEG segments, and N is the weight percentage of PBT segments) has PEG blocks or segments that can form hydrogen-bonding with PEA molecules in that the oxygen atom in PolyActive™ can act as a donor atom to form a hydrogen bond as shown below:

The carbonyl oxygens in the ester linkages of PolyActive™ can also act as hydrogen bond donor atoms. As a result, the T_(g) of the PEA/PolyActive™ blend will be higher than that of PEA. In addition, the PEA component in the blend will have drug-release properties better than PolyActive™ alone because PolyActive™ does not give good drug-release control when used alone. In this embodiment, the PEA and PolyActive™ can be used as a blend to coat an implantable device or to form the implantable device itself or in separate layers to coat an implantable device. For example, the PEA/PolyActive™ blend can be coated onto a stent as a drug delivery matrix. Alternatively, the PEA and PolyActive™ can be coated onto an implantable device in separate layers, where, in the interphase between a PolyActive™ and a PEA layer, the hydrogen-bonding shown above may still exist between the PolyActive molecules and the PEA molecules at the interface. In one embodiment, the PEA can be conjugated to a biobeneficial moiety. The biobeneficial moiety is derived from a biobeneficial material defined below. For example, the PEA/biobeneficial moiety conjugate can be PEA-PEG, PEA-phosphoryl choline (PEA-PC), or PEA-choline.

In some other embodiments, dendrimers and/or star-shaped polymers having —NH₂ or —COOH pendant or end groups can be blended into PEA to facilitate hydrogen-bonding. The star polymers or dendrimers can contain a conjugated active agent in addition to the hydrogen bonding moieties such as —COOH or —NH₂. Other filler materials such as an absorbable glass with Fe, Ca and/or P can be blended into a PEA polymer. The electrostatic interaction may also enhance the T_(g) of the blend thus formed.

In some embodiments, the hydrogen-bonding filler polymers can be a bioactive component that would modulate biological outcome additively or synergistically with a drug in a drug-delivery coating formed of a PEA polymer. Such bioactive component can be, for example, laminin V, silk elastin, or hyaluronic acid-benzyl ester for faster healing, resten NG, or other antisense oligonucleotide fragment with antiproliferative properties, MMPI for preventing SMC migration, and/or cellulose acetate-co-pentasaccharide for local factor Xa inhibition, etc.

Biobeneficial Material

The PEA with hydrogen-bonding fillers can form a coating optionally with a biobeneficial material. The combination can be mixed, blended, or coated in separate layers. The biobeneficial material useful in the coatings described herein can be a polymeric material or non-polymeric material. The biobeneficial material is preferably non-toxic, non-antigenic and non-immunogenic. A biobeneficial material is one that enhances the biocompatibility of a device by being non-fouling, hemocompatible, actively non-thrombogenic, or anti-inflammatory, all without depending on the release of a pharmaceutically active agent.

Representative biobeneficial materials include, but are not limited to, polyethers such as poly(ethylene glycol), copoly(ether-esters) (e.g. PEO/PLA); polyalkylene oxides such as poly(ethylene oxide), poly(propylene oxide), poly(ether ester), polyalkylene oxalates, polyphosphazenes, phosphoryl choline, choline, poly(aspirin), polymers and co-polymers of hydroxyl bearing monomers such as hydroxyethyl methacrylate (HEMA), hydroxypropyl methacrylate (HPMA), hydroxypropylmethacrylamide, poly (ethylene glycol) acrylate (PEGA), PEG methacrylate, 2-methacryloyloxyethylphosphorylcholine (MPC) and n-vinyl pyrrolidone (VP), carboxylic acid bearing monomers such as methacrylic acid (MA), acrylic acid (AA), alkoxymethacrylate, alkoxyacrylate, and 3-trimethylsilylpropyl methacrylate (TMSPMA), poly(styrene-isoprene-styrene)-PEG (SIS-PEG), polystyrene-PEG, polyisobutylene-PEG, polycaprolactone-PEG (PCL-PEG), PLA-PEG, poly(methyl methacrylate)-PEG (PMMA-PEG), polydimethylsiloxane-co-PEG (PDMS-PEG), poly(vinylidene fluoride)-PEG (PVDF-PEG), PLURONIC™ surfactants (polypropylene oxide-co-polyethylene glycol), poly(tetramethylene glycol), hydroxy functional poly(vinyl pyrrolidone), biomolecules such as fibrin, fibrinogen, cellulose, starch, collagen, dextran, dextrin, hyaluronic acid, fragments and derivatives of hyaluronic acid, heparin, fragments and derivatives of heparin, glycosamino glycan (GAG), GAG derivatives, polysaccharide, elastin, chitosan, alginate, silicones, and combinations thereof. In some embodiments, the coating can exclude any one of the aforementioned polymers.

In a further embodiment, the biobeneficial material can be garlic oil, fullerene, metallic materials such as Ca, Mg, and Tantalum ions.

In a preferred embodiment, the biobeneficial material can include a polyether such as poly(ethylene glycol) (PEG) or polyalkylene oxide.

Bioactive Agents

The polymeric coatings or the polymeric substrate described herein may optionally include one or more bioactive agents. These bioactive agents can be any agent which is a therapeutic, prophylactic, or diagnostic agent. These agents can have anti-proliferative or anti-inflammatory properties or can have other properties such as antineoplastic, antiplatelet, anti-coagulant, anti-fibrin, antithrombonic, antimitotic, antibiotic, antiallergic, antioxidant as well as cystostatic agents. Examples of suitable therapeutic and prophylactic agents include synthetic inorganic and organic compounds, proteins and peptides, polysaccharides and other sugars, lipids, and DNA and RNA nucleic acid sequences having therapeutic, prophylactic or diagnostic activities. Nucleic acid sequences include genes, antisense molecules that bind to complementary DNA to inhibit transcription, and ribozymes. Some other examples of other bioactive agents include antibodies, receptor ligands, enzymes, adhesion peptides, blood clotting factors, inhibitors or clot dissolving agents such as streptokinase and tissue plasminogen activator, antigens for immunization, hormones and growth factors, oligonucleotides such as antisense oligonucleotides and ribozymes and retroviral vectors for use in gene therapy. Examples of anti-proliferative agents include rapamycin and its functional or structural derivatives, 40-O-(2-hydroxy)ethyl-rapamycin (everolimus), and its functional or structural derivatives, paclitaxel and its functional and structural derivatives. Examples of rapamycin derivatives include methyl rapamycin (ABT-578), 40-O-(3-hydroxy)propyl-rapamycin, 40-O-[2-(2-hydroxy)ethoxy]ethyl-rapamycin, and 40-O-tetrazole-rapamycin. Examples of paclitaxel derivatives include docetaxel. Examples of antineoplastics and/or antimitotics include methotrexate, azathioprine, vincristine, vinblastine, fluorouracil, doxorubicin hydrochloride (e.g. Adriamycin® from Pharmacia & Upjohn, Peapack N.J.), and mitomycin (e.g. Mutamycin® from Bristol-Myers Squibb Co., Stamford, Conn.). Examples of such antiplatelets, anticoagulants, antifibrin, and antithrombins include sodium heparin, low molecular weight heparins, heparinoids, hirudin, argatroban, forskolin, vapiprost, prostacyclin and prostacyclin analogues, dextran, D-phe-pro-arg-chloromethylketone (synthetic antithrombin), dipyridamole, glycoprotein IIb/IIIa platelet membrane receptor antagonist antibody, recombinant hirudin, thrombin inhibitors such as Angiomax ä (Biogen, Inc., Cambridge, Mass.), calcium channel blockers (such as nifedipine), colchicine, fibroblast growth factor (FGF) antagonists, fish oil (omega 3-fatty acid), histamine antagonists, lovastatin (an inhibitor of HMG-CoA reductase, a cholesterol lowering drug, brand name Mevacor® from Merck & Co., Inc., Whitehouse Station, N.J.), monoclonal antibodies (such as those specific for Platelet-Derived Growth Factor (PDGF) receptors), nitroprusside, phosphodiesterase inhibitors, prostaglandin inhibitors, suramin, serotonin blockers, steroids, thioprotease inhibitors, triazolopyrimidine (a PDGF antagonist), nitric oxide or nitric oxide donors, super oxide dismutases, super oxide dismutase mimetic, 4-amino-2,2,6,6-tetramethylpiperidine-1-oxyl (4-amino-TEMPO), estradiol, anticancer agents, dietary supplements such as various vitamins, and a combination thereof. Examples of anti-inflammatory agents including steroidal and non-steroidal anti-inflammatory agents include tacrolimus, dexamethasone, clobetasol, combinations thereof. Examples of such cytostatic substance include angiopeptin, angiotensin converting enzyme inhibitors such as captopril (e.g. Capoten® and Capozide® from Bristol-Myers Squibb Co., Stamford, Conn.), cilazapril or lisinopril (e.g. Prinivil® and Prinzide® from Merck & Co., Inc., Whitehouse Station, N.J.). An example of an antiallergic agent is permirolast potassium. Other therapeutic substances or agents which may be appropriate include alpha-interferon, bioactive RGD, and genetically engineered epithelial cells. The foregoing substances can also be used in the form of prodrugs or co-drugs thereof. The foregoing substances are listed by way of example and are not meant to be limiting. Other active agents which are currently available or that may be developed in the future are equally applicable.

The dosage or concentration of the bioactive agent required to produce a favorable therapeutic effect should be less than the level at which the bioactive agent produces toxic effects and greater than the level at which non-therapeutic results are obtained. The dosage or concentration of the bioactive agent can depend upon factors such as the particular circumstances of the patient; the nature of the trauma; the nature of the therapy desired; the time over which the ingredient administered resides at the vascular site; and if other active agents are employed, the nature and type of the substance or combination of substances. Therapeutic effective dosages can be determined empirically, for example by infusing vessels from suitable animal model systems and using immunohistochemical, fluorescent or electron microscopy methods to detect the agent and its effects, or by conducting suitable in vitro studies. Standard pharmacological test procedures to determine dosages are understood by one of ordinary skill in the art.

Examples of Implantable Devices

As used herein, an implantable device may be any suitable medical substrate that can be implanted in a human or veterinary patient. Examples of such implantable devices include self-expandable stents, balloon-expandable stents, stent-grafts, grafts (e.g., aortic grafts), artificial heart valves, cerebrospinal fluid shunts, pacemaker electrodes, and endocardial leads (e.g., FINELINE and ENDOTAK, available from Guidant Corporation, Santa Clara, Calif.). The underlying structure of the device can be of virtually any design. The device can be made of a metallic material or an alloy such as, but not limited to, cobalt chromium alloy (ELGILOY), stainless steel (316L), high nitrogen stainless steel, e.g., BIODUR 108, cobalt chrome alloy L-605, “MP35N,” “MP20N,” ELASTINITE (Nitinol), tantalum, nickel-titanium alloy, platinum-iridium alloy, gold, magnesium, or combinations thereof. “MP35N” and “MP20N” are trade names for alloys of cobalt, nickel, chromium and molybdenum available from Standard Press Steel Co., Jenkintown, Pa. “MP35N” consists of 35% cobalt, 35% nickel, 20% chromium, and 10% molybdenum. “MP20N” consists of 50% cobalt, 20% nickel, 20% chromium, and 10% molybdenum. Devices made from bioabsorbable or biostable polymers could also be used with the embodiments of the present invention. The device itself, such as a stent, can also be made from the described inventive polymers or polymer blends.

Method of Use

In accordance with embodiments of the invention, a coating of the various described embodiments can be formed on an implantable device or prosthesis, e.g., a stent. For coatings including one or more active agents, the agent will remain on the medical device such as a stent during delivery and expansion of the device, and released at a desired rate and for a predetermined duration of time at the site of implantation. Preferably, the medical device is a stent. A stent having the above-described coating is useful for a variety of medical procedures, including, by way of example, treatment of obstructions caused by tumors in bile ducts, esophagus, trachea/bronchi and other biological passageways. A stent having the above-described coating is particularly useful for treating occluded regions of blood vessels caused by abnormal or inappropriate migration and proliferation of smooth muscle cells, thrombosis, and restenosis. Stents may be placed in a wide array of blood vessels, both arteries and veins. Representative examples of sites include the iliac, renal, and coronary arteries.

For implantation of a stent, an angiogram is first performed to determine the appropriate positioning for stent therapy. An angiogram is typically accomplished by injecting a radiopaque contrasting agent through a catheter inserted into an artery or vein as an x-ray is taken. A guidewire is then advanced through the lesion or proposed site of treatment. Over the guidewire is passed a delivery catheter which allows a stent in its collapsed configuration to be inserted into the passageway. The delivery catheter is inserted either percutaneously or by surgery into the femoral artery, brachial artery, femoral vein, or brachial vein, and advanced into the appropriate blood vessel by steering the catheter through the vascular system under fluoroscopic guidance. A stent having the above-described coating may then be expanded at the desired area of treatment. A post-insertion angiogram may also be utilized to confirm appropriate positioning.

EXAMPLES

The embodiments of the present invention will be illustrated by the following set forth examples. All parameters and data are not to be construed to unduly limit the scope of the embodiments of the invention.

Example 1 Study of Stents Coated with the Combination of Poly(ester amide) and PolyActive™

Vision 12 mm small stents (available from Guidant Corporation) are coated according to the following configurations:

Configuration 1

Primer layer: 100 μg PolyActive™, from a 2% PolyActive™ (300PEGT55PBT45) solution in a solvent mixture of 1,1,2-trichloroethane and chloroform (80/20) (w/w), and baked at 50° C. for 1 hour;

Drug layer: 120 μg everolimus, coated from a 2% drug solution dissolved in a solvent mixture of acetone/xylene (60/40) (w/w), baked at 50° C. for 1 hour;

PEA release rate control layer: 100 μg PEA, coated from a 2% PEA solution in ethanol; baked at 50° C. for 1 hour;

PolyActive™ biobeneficial layer: 200 μg PolyActive™, coated from a 2% PolyActive™ (300PEGT55PBT45) solution in a solvent mixture of 1,1,2-trichloroethane and chloroform (80/20) (w/w), and baked at 50° C. for 1 hour.

Configuration 2

Primer layer: 100 μg PolyActive™, from a 2% PolyActive™ (300PEGT55PBT45) solution in a solvent mixture of 1,1,2-trichloroethane and chloroform (80/20) (w/w), and baked at 50° C. for 1 hour;

Drug layer: 120 μg everolimus, coated from a 2% drug solution dissolved in a solvent mixture of acetone/xylene (60/40) (w/w), and baked at 50° C. for 1 hour;

PEA release rate control layer: 200 μg PEA, coated from a 2% PEA solution in ethanol; baked at 50° C. for 1 hour;

PolyActive™ biobeneficial layer: 200 μg PolyActive™, coated from a 2% PolyActive™ (300PEGT55PBT45) solution in a solvent mixture of 1,1,2-trichloroethane and chloroform (80/20) (w/w), and baked at 50° C. for 1 hour.

Configuration 3

Primer layer: 100 μg PolyActive™, from a 2% PolyActive™ (300PEGT55PBT45) solution in a solvent mixture of 1,1,2-trichloroethane and chloroform (80/20) (w/w), and baked at 50° C. for 1 hour;

Drug layer: 120 μg everolimus, coated from a 2% drug solution dissolved in a solvent mixture of acetone/xylene (60/40) (w/w), and baked at 50° C. for 1 hour;

PEA release rate control layer: 400 μg PEA, coated from a 2% (w/w) PEA solution in ethanol; baked at 50° C. for 1 hour;

PolyActive™ biobeneficial layer: 200 μg PolyActive™, coated from a 2% PolyActive™ (300PEGT55PBT45) solution in a solvent mixture of 1,1,2-trichloroethane and chloroform (80/20) (w/w), and baked at 50° C. for 1 hour.

The stents coated according to the above configurations are shown in FIGS. 1 a, 1 b and 1 c, which show the good mechanical integrity of these coatings. The stents were subjected to an in vitro drug release study. FIG. 2 shows the release profile of these coatings in a PBS-Triton buffer system. The data from porcine serum are listed in Table 1. The results showed that the coating of configuration 1 released about 25% of the drug on day one and 75% on day two. A linear release profile was observed for all the coatings. It is noteworthy that the release rate decreases in a linear relationship to the amount of PEAs used in the coatings (Configuration 1: 100 μg PEA, Configuration 2: 200 μg PEA, and Configuration 3: 400 μg PEA), clearly showing membrane controlled drug release characteristics.

TABLE 1 Drug release rate in porcine serum after 24 and 72 hours Sample Configuration 1 Configuration 2 Configuration 3 Time 24 hr 72 hr 24 hr 72 hr 24 hr 72 hr Release % 25.9% 73% 12.4% NA 8.4% NA

Example 2 Stents Coated with PEA-TEMPO

A first composition is prepared by mixing the following components:

-   (a) about 2.0% (w/w) of the polymer PEA-TEMPO -   (b) the balance, ethyl alcohol

The first composition can be applied onto the surface of bare 12 mm small VISION™ stent (Guidant Corp.). The coating can be sprayed and dried to form a primer layer. A spray coater can be used having a 0.014 round nozzle maintained at ambient temperature with a feed pressure 2.5 psi (0.17 atm) and an atomization pressure of about 15 psi (1.02 atm). About 20 μg of the coating can be applied per one spray pass. Between spray passes, the stent can be dried for about 10 seconds in a flowing air stream at about 50° C. About 110 μg of wet coating can be applied. The stents can be baked at about 50° C. for about one hour, yielding a primer layer composed of approximately 100 μg of PEA-TEMPO.

Example 3 Stents Coated with PEA-TEMPO and Poly(imino carbonate)

A second composition can be prepared by mixing the following components:

(a) about 1.8% (w/w) of the polymer of PEA-TEMPO;

(b) about 0.2% (w/w) of poly(imino carbonate)

(b) about 0.5% (w/w) of everolimus; and

(c) the balance, a solvent mixture of ethyl alcohol and dimethylformamide (80/20) (w/w)

The second composition can be applied onto the dried primer layer to form the drug-polymer layer, using the same spraying technique and equipment used for applying the primer layer. About 300 μg of wet coating can be applied followed by drying and baking at about 60° C. for about 2 hours, yielding a dry drug-polymer layer having solids content of about 275 μg.

While particular embodiments of the present invention have been shown and described, it will be obvious to those skilled in the art that changes and modifications can be made without departing from this invention in its broader aspects. Therefore, the appended claims are to encompass within their scope all such changes and modifications as fall within the true spirit and scope of this invention. 

1. An implantable device comprising a coating, the coating comprising: a poly(ester amide) (PEA) polymer comprising a polymer chain having amide groups in the chain, and a material for hydrogen-bonding with the PEA, wherein the polymer chain of one molecule of the PEA polymer hydrogen-bonds to a molecule of the material for hydrogen-bonding, which in turn hydrogen-bonds to the polymer chain of another molecule of the PEA polymer.
 2. The implantable device of claim 1, wherein the PEA polymer comprises diacid, diol, and amino acid subunits in its backbone.
 3. The implantable device of claim 1, wherein the PEA polymer is co-poly-{[N,N′-sebacoyl-bis-(L-leucine)-1,6-hexylene diester]-[N,N′-sebacoyl-L-lysine benzyl ester]}(PEA-Bz) or co-poly{[N,N′-sebacoyl-bis-(L-leucine)-1,6-hexylene diester]-[N,N′-sebacoyl-L-lysine 4-amino-TEMPO amide]}(PEA-TEMPO).
 4. The implantable device of claim 3, further comprising a biobeneficial material selected from garlic oil, fullerene, heparin, hirudin, fibrin, hyaluronic acid, hydrophobically modified hyaluronic acid, chondroitan sulfate, glycosaminoglycans, chitin, poly(styrene sulfonate), or combinations thereof.
 5. The implantable device of claim 1, wherein the material for hydrogen-bonding with PEA is selected from the group consisting of non-degradable polymers, biodegradable polymers and combinations thereof, wherein the non-degradable polymer has a molecular weight below about 40,000 Daltons, and wherein the biodegradable polymer can degrade into fragments having a molecular weight below about 40,000 Daltons.
 6. The implantable device of claim 1, wherein the material for hydrogen-bonding with PEA is selected from the group consisting of polymers or copolymers of monomers containing a hydroxyl group, a carboxyl group, an ether group, a carbonyl group, a urethane group, a urea group, or an amino group, poly(vinyl alcohol), poly(vinyl alcohol-co-vinyl acetate), polyacrylic acid, polymethacrylic acid, poly(acrylamide), poly(hydroxypropyl methacrylamide), poly(2-hydroxyethyl methacrylate), poly(2-methoxyethyl methacrylate), poly(2-ethoxyethyl methacrylate), poly(2-methoxyethyl acrylate), poly(vinyl pyrrolidone), poly(pyrrole), poly(ethylene-co-vinyl alcohol), non-water soluble cellulose acetate, non-water soluble hydroxyethyl cellulose, non-water soluble hydroxypropyl cellulose, cellulose ethers, methyl cellulose and ethyl cellulose, poly(urethanes), poly(urethane-ureas), poly(ureas), poly(tetramethylene glycol), poly(propylene glycol), poly(ethylene glycol), poly(imino carbonates), peptides, gelatin, collagen, non-water soluble chitosan, agarose, elastin, poly(alginic acid), alginate, dextrose, dextran, poly(glutamic acid), poly(lysine), copolymers containing poly(ethylene glycol) and polybutylene terephthalate segments, poly(aspartic acid), poly(leucine), poly(leucine-co-hydroxyethyl glutamine), poly(benzyl glutamate), poly(glutamic acid-co-ethyl glutamate), poly(amino acids), poly(ortho esters), poly(anhydrides), poly(D,L-lactic acid), poly (L-lactic acid), poly(glycolic acid), copolymers of poly(lactic) and glycolic acid, poly(phospho esters), poly(-hydroxybutyrate), poly(caprolactone), poly(trimethylene carbonate), poly(oxaesters), poly(oxaamides), poly(ethylene carbonate), poly(propylene carbonate), poly(phosphoesters), poly(phosphazenes), copolymers thereof with poly(ethylene glycol), and combinations thereof.
 7. The implantable device of claim 1, wherein the material for hydrogen-bonding with PEA is a-copolymer containing poly(ethylene glycol) and polybutylene terephthalate segments.
 8. The implantable device of claim 7, wherein the PEA and the copolymer containing poly(ethylene glycol) and polybutylene terephthalate segments form a blend.
 9. The implantable device of claim 7, wherein the PEA forms a PEA layer of coating, and wherein the copolymer containing poly(ethylene glycol) and polybutylene terephthalate segments forms a layer of coating separate from the PEA layer of coating.
 10. The implantable device of claim 1, further comprising a biobeneficial material selected from garlic oil, fullerene, heparin, hirudin, fibrin, hyaluronic acid, hydrophobically modified hyaluronic acid, chondroitan sulfate, glycosaminoglycans, chitin, poly(styrene sulfonate), or combinations thereof.
 11. The implantable device of claim 1, further comprising a biobeneficial material garlic oil, fullerene, heparin, hirudin, fibrin, hyaluronic acid, hydrophobically modified hyaluronic acid, chondroitan sulfate, glycosaminoglycans, chitin, poly(styrene sulfonate), or combinations thereof.
 12. The implantable device of claim 1, wherein the material for hydrogen bonding with PEA is selected from the group consisting of dendrimers, star-shaped molecules, absorbable glass, and combinations thereof, wherein the dendrimer or star-shaped molecule has a group selected from the group consisting of —NH₂, —COOH, —OH groups and combinations thereof, and wherein the absorbable glass comprises Fe, Ca, or phosphate, or combinations thereof.
 13. The implantable device of claim 1, wherein the material for hydrogen bonding with PEA is a bioactive component selected from the group consisting of laminin V, silk elastin, hyaluronic acid-benzyl ester, resten NG, antisense oligonucleotide fragment with antiproliferative properties, MMPI, cellulose acetate-co-pentasaccharide, and combinations thereof.
 14. The implantable device of claim 1, wherein the implantable device is a stent.
 15. The implantable device of claim 14, wherein the coating further comprises a therapeutic agent.
 16. The implantable device of claim 15, wherein the therapeutic agent is selected from the group consisting of paclitaxel, docetaxel, estradiol, nitric oxide donors, super oxide dismutases, super oxide dismutases mimics, 4-amino-2,2,6,6-tetramethylpiperidine-1-oxyl(4-amino-TEMPO), tacrolimus, dexamethasone, rapamycin, rapamycin derivatives, 40-O-(2-hydroxy)ethyl-rapamycin (everolimus), 40-O-(3 -hydroxy)propyl-rapamycin, 40-O-[2-(2-hydroxy)ethoxy]ethyl-rapamycin, and 40-O-tetrazole -rapamycin, ABT-578, clobetasol, progenitor cell capturing antibody, prohealing drugs, prodrugs thereof, co-drugs thereof, and a combination thereof. 